Aluminum Composite Panel for Building Cladding, Interior and Exterior, Indoor and Outdoor

Product Description

Company Information:
Henan Jixiang Industry Co., Ltd; Henan Aludong Decorative Materials Co.,Ltd is located in Zhengzhou City,Henan Province, Which a professional enterprise manufacturing high and new-tech aluminum composite products,which is one of the earliest and scaled manufacturers of aluminum composite, coated aluminum coils, aluminum solid panel in China.
Our company possesses16 production lines and 6 coating lines for aluminum composite panels whose annual output is 5.8million square meters.In addition, our company has passed ISO9001 International Quality Management System Certification, ISO14000 Environment Management System Certification, OHSAS18000 Occupation Health Safety Management System Certification, and CTC Product Quality Certification, and won several national patents.
ALUDONG Product information:
Aludong Aluminum composite panel is made of aluminum alloy and plastic material to feature great hardness, light weight and smooth service, provided with wide range of sizes, shapes, colors, and styles to offer broader options for construction design, in a bid to better meet the requirements of contemporary construction on lightweight, elegant decoration and high hardness
Aluminum composite panel is widely used in all kinds of architectural decorations for its excellent properties, such as the, cladding, shops front, ceiling, counters, furniture, road signs, billboards, kiosks, elevators, stores.
ALUDONG Product range:

Surface Coating	Polyester/ PVDF /Nano/ FEVE
Aluminum Alloy	AA1100, AA3003, AA5005
Aluminum Skin	0.10mm,0.12mm,0.15mm,0.18mm,0.21mm,0.25mm,0.30mm 0.40mm,0.50mm
Panel Thickness	2mm,3mm,4mm,5mm,6mm ; Range from 2-8mm
Core Material	Non-toxic low density polyethylene; non-combustible core
Panel Width	1000mm,1220mm,1250mm,1500mm,1550mm
Panel Length	2440mm,3050mm,4000mm,5000mm
Back Coat	PE coating, Primer Coating ,Mill finish

Aluminum composite panel is suitable for both exterior and interior architectural and signs applications,.PVDF coated for exterior and Polyester coated for interior applications, as well as for industrial and special product design. Consider them for exterior cladding, clean rooms, signage, corporate logos, column covers, interior partitions, canopies, equipment enclosures, kiosks, exhibition and display platforms.

ALUMINUM COMPOSITE PANEL SPECIFICATION
PANAEL ALU	1220MM WIDTH				1220/1500/1550MM WIDTH
	PE COAT					PVDF / NANO-PVDF COAT
2MM	0.08	0.10	0.12	0.15	0.18	0.21	/	/	/	/	/	/
3MM	0.08	0.10	0.12	0.15	0.18	0.21	0.25	0.30	0.35	0.40	/	/
4MM	/	0.10	0.12	0.15	0.18	0.21	0.25	0.30	0.35	0.40	0.45	0.50
5MM	/	0.10	0.12	0.15	0.18	0.21	0.25	0.30	0.35	0.40	0.45	0.50
6MM	/	0.10	0.12	0.15	0.18	0.21	0.25	0.30	0.35	0.40	0.45	0.50
7MM	/	0.10	0.12	0.15	0.18	0.21	0.25	0.30	0.35	0.40	0.45	0.50
8MM	/	0.10	0.12	0.15	0.18	0.21	0.25	0.30	0.35	0.40	0.45	0.50

ALUDONG Products tolerance:

Panel Width	±2mm
Panel Length	±3mm
Panel Thickness	±0.2mm
Panel Diagonal	≤ 5mm
Aluminum layer thickness	±0.02mm

ALUDONG Technical data for Polyester Coating:

Description	Test standard	Polyester
Coating Thickness (μm)	Polyester paint >=16μm	16μm to 18μm
Coating flexibility (T-bend)	Polyester paint ≤ 3T	≤ 3T
Color different	ΔE<=2.0 (follow color sample)	ΔE<=2.0
Pencil hardness	>=HB	>=2H
Chemical resistance	2%HCI or 2%NaOH test in 24 hours -No change	No change
Coating adhesion	>=1grade for 10810mm2 gridding test	1grade
Resist solvent	100 times without change	No change
Boiling water resistance	2 hours without change	No change
Peeling strength/stripping strength	Average >=5N/mm of 180oc peel off for panel with 0.21mm alu.skin	5N/mm
Impact test for paint	20KG.cm impact-paint no split for panel	No split
Abrasion resistance (L/Mil)	NIL	NIL
Temperature resistance	-40ºC to +80ºC temperature without change of color difference and paint peel off , peeling strength average dropprate<=10%	Change of glossy only, no paint Peel off
Coefficient of linear Thermal Expansion	100ºC temperature difference	2.4mm/n
Detergent resistance (3%)	ASTM D2248	No change
Humidity Resistance	ASTM D2247 (2000hrs,100%RH,100°F)	No change
Salt spray resistance	ASTM B117 (2000hrs,2% salt)	No change
Resistance to Staining	600h radiate in 800W/M2 in humidity condition, glossiness deviation less grade 2,color difference <=4.0	No change

ALUDONG Technical data for PVDF Coating:

Description	Test standard	PVDF
Coating Thickness (μm)	Polyester paint >=25μm	26μm
Coating flexibility (T-bend)	Polyester paint ≤ 3T	≤ 2T
Color different	ΔE<=2.0 (follow color sample)	ΔE<=2.0
Pencil hardness	>=HB	>=2H
Chemical resistance	5%HCI or 5%NaOH test in 48 hours -No change	No change
Coating adhesion	>=1grade for 10810mm2 gridding test	1grade
Resist solvent	100 times without change	No change
Boiling water resistance	2 hours without change	No change
Peeling strength/stripping strength	Average >=5N/mm of 180oc peel off for panel with 0.30mm alu.skin	5N/mm
Impact test for paint	50KG.cm impact-paint no split for panel	No split
Abrasion resistance (L/Mil)	NIL	NIL
Temperature resistance	-40ºC to +80ºC temperature without change of color difference and paint peel off , peeling strength average dropprate<=10%	Change of glossy only, no paint Peel off
Coefficient of linear Thermal Expansion	100ºC temperature difference	2.4mm/n
Detergent resistance (3%)	ASTM D2248	No change
Humidity Resistance	ASTM D2247 (3000hrs,100%RH,100°F)	No change
Salt spray resistance	ASTM B117 (3000hrs,5% salt)	No change
Resistance to Staining	600h radiate in 800W/M2 in humidity condition, glossiness deviation less grade 2,color difference <=4.0	No change

Exhibition:
Pls contact:
Manager: Jason Lee